WEPWB043 | Nb3Sn Vapor Diffusion Coating System at SARI: Design, Construction, and Commissioning | 655 |
SUSPB038 | use link to see paper's listing under its alternate paper code | |
|
||
This paper describes the design of a coating system for the preparation of a superconducting radio-frequency cavity with Nb3Sn thin films. The device consists of a coating chamber made of pure niobium, a vacuum furnace for heating the coating chamber, a superconducting cavity bracket and two crucible heaters. The chamber is vacuum isolated from the furnace body to protect the superconducting cavity from contamination during the coating process. The device has been built and commissioned, which could be used for Nb₃Sn coating of a 1.3 GHz single-cell superconducting cavity in future. | ||
DOI • | reference for this paper ※ doi:10.18429/JACoW-SRF2023-WEPWB043 | |
About • | Received ※ 19 June 2023 — Revised ※ 22 June 2023 — Accepted ※ 26 June 2023 — Issue date ※ 08 July 2023 | |
Cite • | reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml) | |
WEPWB044 | Realization of Accelerating Gradient Larger than 25 MV/m on High-Q 1.3 GHz 9-Cell Cavities for SHINE | 658 |
SUSPB039 | use link to see paper's listing under its alternate paper code | |
|
||
Funding: This work was supported by Shanghai Municipal Science and Technology Major Project (No. 2017SHZDZX02). We present our studies on the optimized nitrogen-doping and medium-temperature baking recipes applied on 1.3GHz SRF cavities, aiming at meeting the requirements of the SHINE project. The optimized nitrogen-doping process resulted in achieving a Q₀ of over 4.0×1010 at medium field and a maximum accelerating gradient exceeding 35 MV/m on single cell cavities, and a Q₀ of over 2.8×1010 at medium field and a maximum accelerating gradient exceeding 26 MV/m in 9-cell cavities. For 1.3 GHz 9-cell cavities subjected to medium-temperature baking, Q₀ values exceeding 3.5×1010 at 16 MV/m and maximum accelerating gradients surpassing 25 MV/m were achieved. These studies provide two options of high-Q recipes for SHINE cavities. The treatment processes of cavities and their vertical test results are described in this paper. *chenjinfang@sari.ac.cn |
||
DOI • | reference for this paper ※ doi:10.18429/JACoW-SRF2023-WEPWB044 | |
About • | Received ※ 19 June 2023 — Revised ※ 22 June 2023 — Accepted ※ 26 June 2023 — Issue date ※ 26 June 2023 | |
Cite • | reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml) | |
THIAA01 | Development of 3.9 GHz 9-Cell Cavities at SHINE | 921 |
|
||
The Shanghai high-repetition-rate XFEL and extreme light facility (SHINE) Linac requires two 3.9~GHz crymodules to linearize energy distribution before the bunch compressor. As a key component to the project, studies of 3.9~GHz cavities were conducted in the past few years. The first 3.9~GHz 9-cell prototype cavity has been fabricated, tested, and qualified. It reached Q0=3.5×109 at 13.1~MV/m and a maximum accelerating gradient of 25.0~MV/m during the vertical test of the bare cavity. The prototype has been helium tank integrated and reached Q0=2.9×109 at 13.1~MV/m in the vertical test, with a large margin with respect to the SHINE specification. The second prototype has been fabricated and is planned to be tested in 2023. This paper will cover the fabrication, surface treatment, and RF test of the 3.9~GHz cavities. | ||
Slides THIAA01 [7.573 MB] | ||
DOI • | reference for this paper ※ doi:10.18429/JACoW-SRF2023-THIAA01 | |
About • | Received ※ 19 June 2023 — Revised ※ 24 June 2023 — Accepted ※ 28 June 2023 — Issue date ※ 18 July 2023 | |
Cite • | reference for this paper using ※ BibTeX, ※ LaTeX, ※ Text/Word, ※ RIS, ※ EndNote (xml) | |